Efeito da largura temporal de pulso do Laser de Er: YAG nas características de superfície, adesão e propriedades mecânicas da zircônia / Effect of temporal width pulse of Er: YAG laser on surface characteristics, bond strength and mechanical properties of zirconia

Este estudo avaliou os efeitos da variação da largura temporal de pulso do laser de Er:YAG nas características de superfície (morfologia, transformação de fase, rugosidade e perda de superfície), na resistência de união de um cimento resinoso (Panavia F 2.0, Kuraray, Okayama, Japão) e nas propriedades mecânicas (resistência à fratura) de uma zircônia. Blocos de 3Y-TZP parcialmente sinterizados foram seccionados até a obtenção de 350 espécimes padronizados que foram distribuídos aleatoriamente em sete grupos experimentais, conforme o tratamento de superfície (n=50): GC (sem tratamento); G50 (80mJ/2Hz/50?s); G100 (80mJ/2Hz/100?s); G300 (80mJ/2Hz/300?s); G600 (80mJ/2Hz/600?s) GUNTC (abrasão trioboquímica pré-sinterizado); GTC (abrasão trioboquímica sinterizado). Após os tratamentos, os espécimes foram sinterizados de acordo com as recomendações do fabricante, exceto o grupo GTC, no qual os espécimes foram sinterizados antes do tratamento de superfície. Os espécimes foram avaliados por diferentes métodos, a saber: análise morfológica por microscopia eletrônica de varredura (MEV) (n=3); rugosidade e perda de superfície, por perfilometria óptica 3D (n=8); resistência de união, por ensaio de microcisalhamento (?SBS), em 24 horas e após 8 meses de envelhecimento em água destilada em estufa a 37ºC (n=8); avaliação da transformação de fase por difração de raios-x (DRX) (n=1); e resistência à fratura por teste de flexão biaxial (BFS) (n=30). A irradiação com o Laser de Er:YAG promoveu uma efetiva ablação em todas as larguras temporais de pulso testadas, produzindo superfícies muito irregulares, semelhantes entre si, sem a presença de trincas ou carbonização. A análise dos grupos irradiados (G50, G100, G300 e G600) revelou um aumento estatisticamente significante de rugosidade e de perda de superfície quando comparados aos grupos GC, GUNTC e GTC, o que poderia comprometer a adaptação de peças protéticas. Com relação a ?SBS em 24h, os maiores valores foram observados para o GTC seguido do G300. Enquanto os grupos G50, G100 e G600 apresentaram valores intermediários. Os menores valores foram observados para os grupos GC e GUNTC. Por outro lado, para todos os grupos experimentais testados a ?SBS decresceu após 8 meses de armazenamento. Nos padrões de DRX foram observados picos de difração correspondentes ao conteúdo monoclínico somente para o grupo GTC, nos outros grupos foram observados apenas conteúdo de zircônia tetragonal. Os valores médios de BFS apresentaram diferença estatisticamente significante para os grupos estudados, sendo que os maiores valores foram observados no GTC. Os grupos irradiados (G50, G100, G300 e G600) apresentaram uma diminuição da BFS. Já os grupos sem tratamento (GC) e GUNTC apresentaram valores de BFS intermediários. A irradiação com as diferentes larguras de pulso do laser de Er:YAG criou uma superfície rugosa e com grande perda de superfície, a ?SBS entre o cimento resinoso e a Y-TZP não resistiu aos oito meses de armazenamento em água, além de gerar uma diminuição da BFS; portanto, seu uso não é recomendado.

Non-thermal plasma increase bond strength of zirconia to a resin cement / Plasma não-térmico aumenta a resistência de união da zircônia a um cimento resinoso

Objective: This study investigated the influence of different surface treatments on zirconia surface energy, roughness and microshear bond strength. Material and Methods: Forty eight slices of Yttriastabilized tetragonal zirconia polycrystal (Y-TZPVITA In-Ceram® YZ for inLab®) (6.4 x 3.2 x 1.6 mm) were divided into 3 groups according to the surface treatment (n = 16): YTZP_control -untreated; YTZP_plasma -surface treatment with non-thermal oxygen plasma; YTZP_primer - coating with ceramic primer. Surface energy (n = 6) was measured with a goniometer; and surface roughness (n = 10) was analyzed with a 3D profilometer were performed over zirconia surface. On the same specimens of surface roughness, on the treated zirconia's surface, resin cement (PANAVIA V5 - Kuraray Noritake Dental) was built up by inserting the resin cement into Tygon tubes (1 mm of internal diameter X 1 mm length). After 24h storage, microshear test was assessed. Data were analyzed by one-way ANOVA and Tukey posthoc test (p < 0.05). Results: Nonthermal oxygen plasma treated specimens exhibited higher statistically significant surface energy (p = 0.00) and bond strength (p = 0.00) when compared to control and primer groups. Roughness test (p = 0.897) could not detect statistical difference among the tested groups. Conclusion: Non-thermal oxygen plasma should be a suitable alternative for zirconia surface treatment prior to luting hence it improved microshear bond strength and provided higher surface energy without affecting surface roughness. (AU)

Objetivo: Este estudo investigou a influência de diferentes tratamentos de superfície na energia de superfície, rugosidade e resistência de união da zircônia. Material e Métodos: Quarenta e oito fatias de zircônia tetragonal policristalina estabilizada por ítria (Y-TZP - VITA InCeram® YZ for inLab®) (6,4 x 3,2 x 1,6 mm) foram divididas em 3 grupos de acordo com o tratamento de superfície (n = 16): YTZP_controle sem tratamento; YTZP_plasma - tratamento de superfície com plasma de oxigênio não térmico; YTZP_primer - aplicação de um primer cerâmico. A energia da superfície (n = 6) foi medida com o auxilio de um goniômetro; e a rugosidade superficial (n = 10) foi analisada com um perfilômetro 3D. Nos mesmos espécimes da rugosidade, prolongamentos de cimento resinoso (PANAVIA V5 - Kuraray Noritake Dental) foram construídos inserindo o cimento em micro túbulos de silicone (1mm de diâmetro interno de X 1 mm de comprimento). O teste de microcisalhamento foi realizado após 24h. Os dados foram analisados estatisticamente ANOVA um fator e teste auxiliar de Tukey (p < 0,05). Resultados: Os espécimes tratados com plasma de oxigênio apresentaram maiores valores de energia de superficie (p = 0,00) e resistência de união estatisticamente significante (p = 0,00) quando comparados aos grupos controle e do primer. A análise de rugosidade (p = 0,897) não detectou diferença estatística entre os grupos testados. Conclusão: O plasma não térmico pode ser uma alternativa para o tratamento de superfície de zircônia antes da cimentação, pois aumentou a resistência de união ao microcilsalhamento e proporcionou maior energia superficial sem afetar a rugosidade da superfície. (AU)

Bonding efficiency and durability: current possibilities

Abstract Bonding plays a major role in dentistry nowadays. Dental adhesives are used in association with composites to solve many restorative issues. However, the wide variety of bonding agents currently available makes it difficult for clinicians to choose the best alternative in terms of material and technique, especially when different clinical situations are considered. Moreover, although bonding agents allow for a more conservative restorative approach, achieving a durable adhesive interface remains a matter of concern, and this mainly due to degradation of the bonding complex in the challenging oral environment. This review aims to present strategies that are being used or those still in development which may help to prevent degradation. It is fundamental that professionals are aware of these strategies to counteract degradation as much as possible. None of them are efficient to completely solve this problem, but they certainly represent reasonable alternatives to increase the lifetime of adhesive restorations.